OEM Modified PEEK Plate Sheet Engineering Plastic Material

Melting Point : 343 °C

Material : Polyetheretherketone (PEEK)

Color : Natural

Applications : Aerospace, Automotive, Medical, Oil and Gas, Semiconductor

Density : 1.32 g/cm3

UV Resistance : Excellent

Elongation at Break : 3%

Thermal Conductivity : 0.25 W/mK

RoHS Compliant : Yes

Flame Retardant : UL 94 V-0

FDA Compliant : Yes

Water Absorption : <0.01%

Chemical Resistance : Excellent

Tensile Strength : 100 MPa

Flexural Strength : 170 MPa

Brand Name : PRES

Contact Now

PEEK performance index
test item	test standard	test condition	units	PEEK-1000	PEEK-FC1030	PEEK-G1030	PEEK-C1030
				pure resin	filled carbon fiber	filled 30%	filled 30% carbon fiber
					+graphite+PTFE	glass fiber
					(each 10%)
density	ISO 1183	crystallization	g/cm³	1.3	1.44	1.51	1.4
Bibulous rate (3.2mm thick tensile bar immersion test)	ISO 62-1	24h,23°C	%	0.07	0.06	0.04	0.04
Bibulous rate (3.2mm thick tensile bar immersion test)	ISO 62-1	balance,23°C	%	0.4	0.3	0.4	0.3
tensile strength	ISO-527	bend, 23°C	MPa	100	140	175	260
elongation at break	ISO-527	fracture,23°C	%	45	2.2	2.7	1.7
bending strength	ISO-178	bend, 23°C	MPa	165	190	265	380
flexural modulus	ISO-178	23°C	GPa	4.1	7.8	11.3	23
compression strength	ISO-604	23°C	MPa	125	155	250	300
charpy impact	ISO 179/IeA	notched	KJ/m²	7	5	8	7
strength	ISO 179/IU	no notch	KJ/m²			55	45
cantilever beam impact test	ISO 180/A	notched	KJ/m²	7.5	5	10	9
cantilever beam impact test	ISO 180/U	no totch	KJ/m²	—		60	45
shore hardness	ISO 868	23°C	HD	85	80	88	88
melting point	ISO 11357	—	°C	343	343	343	343
glass transition tempreture	ISO 11357	initial point	°C	143	143	143	143
specific heat capacity	DSC	23°C	KJ/kg °C	2.2	1.7	1.7	1.8
coefficient of thermal expansion	ISO 11359	below Tg along the flow direction	ppm/K	45		18	5
coefficient of thermal expansion	ISO 11359	overtopTg along the flow direction	ppm/K	120		18	6
distortion temperature	ISO 75-f	1.8Mpa	°C	152	300	315	315
thermal conductivity	ISO 22007-4	23°C	W/mK	0.29	0.3	0.3	0.95
dielectrical strength	IEC 60243-1	2mm	KV/mm	23		25	—
dielectric constant	IEC 60250	23°C,1KHz	—	3.1		3.2-3.4	—
dielectric constant	IEC 60250	23°C,50HZ	—	3		—	—
volume resistivity	IEC 60093	23°C, 1V	Ω•cm	1016		1016	—
volume resistivity	IEC 60093	275°C	Ω•cm	109		—	—

Product Tags:

OEM peek plate

peek plate Engineering Plastic

modified PEEK Sheet

Quality OEM Modified PEEK Plate Sheet Engineering Plastic Material for sale

OEM Modified PEEK Plate Sheet Engineering Plastic Material Images

Inquiry Cart 0

Send your message to this supplier


*From:	Your email address is incorrect!
*To:	Dongguan Pruisi Plastic Materials Co., Ltd
*Subject:	Subject is empty!
*Message:	For the best results, we recommend including the following details: -Self introduction -Required specifications -Inquire about price/MOQ Characters Remaining: (0/3000) Please enter 20 to 3000 characters to contact this supplier!